English translation for "成型温度"
|
- forming temperature
Related Translations:
冷成型: cold forming process 气压成型: air pressure formingblow moldinggas-pressure compactinggas-pressure compaction 离心成型: centrifugal forming
- Example Sentences:
| 1. | The optimal molding temperature and pressure of their composite are 140c and 7 . 3 mpa
麻纤维复合材料的最佳成型温度为140 ，成型压力7 . 3mpa 。 | | 2. | Both ramie and flax are hydrophilic fibers , their thermal stability is not pretty well
麻纤维素含有大量羟基，亲水性强，热稳定性较差，加工成型温度不宜过高。 | | 3. | The 4 factors , such as specific absorption of aggregate , dosage of fiber , dosage of cement and molding temperature , were assembled properly by orthogonal design method , the effects of the factors on the optimum proportion of asphalt were studied at the same time
采用正交试验方法分析集料吸水率、纤维用量、水泥掺量及成型温度这4个因素对沥青混合料最佳油石比的影响程度。 | | 4. | 4 . the optimistic resin system and the effect of resin content on the targets performance are discussed by orthogonal experiments , based on which , the moulding process parameters such as temperature , pressure , cycle and post - cure temperature are designed optimistically
4 、通过正交试验确定了最佳树脂体系，确定了含胶量对靶板性能的影响，在选定基体材料基础上，通过正交试验分析，对复合材料成型工艺参数如：成型温度、成型压力、成型时间、后处理温度进行了优化设计，确定了体系的最佳成型工艺参数。 | | 5. | The approaches of enhancing the mechanical properties of ramie and flax composites were studied in this paper . the effects of surface pretreatment , fiber content , molding temperature and pressure as well as the effect of electron beam , microwave and ultrasonic wave on the mechanical properties of the composites were explored . the experimental results show that : 1
本文以苎麻、亚麻纤维为增强材料，线性低密度聚乙烯( lldpe )为基体，研制了两种麻纤维层压复合材料，研究了麻织物表面处理、纤维含量、成型温度、成型压力等对该复合材料力学性能的影响，得到了性能较为优异的麻纤维复合材料，探讨了复合材料的增强机理。 |